Non-Tension Bi-Metallic Compression Joints

AL-MM2	A1	A2	L1	CU-MM2	C1	C2	L2	L	Cat. No.
16	6.0	12	33	10	4.5	6	22	55	UTX BML-16/10
25	6.8	12	37	16	5.5	8	24	61	UTX BML-25/16
35	8.0	14	43	25	7.0	10	28	71	UTX BML-35/25
50	10.0	16	43	35	8.2	12	28	71	UTX BML-50/35
70	11.5	18	52	50	10.0	14	34	86	UTX BML-70/50
95	13.5	22	52	70	11.5	16	34	86	UTX BML-95/70
120	15.0	22	59	95	13.5	18	38	97	UTX BML-120/95
150	16.5	25	65	95	13.5	18	43	108	UTX BML-150/95
185	18.5	28	65	120	15.5	20	43	108	UTX BML-185-120
240	21.5	32	75	150	17.0	22	49	124	UTX BML-250/150
300	23.5	34	77	240	21.5	28	51	128	UTX BML-300/240

Conductive Material :

Aluminium Barrel       99.6%
Copper Palm             99.95%
Final Metal State        Fully Annealed including joint.
Joining Method          Friction Welding
Finish                         Natural

Conductivity :

Aluminium      61.8% IACS (MIN)
Copper          99.7% IACS

Aluminium barrel are chemically treated to reduce contact resistance and corrosion and are filled electrically conductive corrosion inhabitant with a jointing compound and capped.

Note :

1. Combinations of Bi-metallic compression joints are designed on the basis of current carrying capacity of individual cables.

2. In case additional combinations are required same may be provided against specific request.

3. Shape, size and dimension are subject to change without notice.