Copper Aluminium Bi-Metal Lugs

Friction Welded

MM2	A	B	C	D	E	F	L	Cat. No.
25	7.5	30	12	20	10.5	5	70	UTX BM-25M10
35	8.5	30	12	20	10.5	5	75	UTX  BM-35M10
50	10.2	32	16	20	10.5	5	80	UTX  BM-50M10
50	10.2	32	16	25	13	5	85	UTX  BM-50M12
70	11.5	45	20	25	13	5	90	UTX  BM-70M12
95	13.5	50	22	25	13	5	95	UTX  BM-95M12
120	15.5	55	22	25	13	5	100	UTX  BM-120M12
150	16.5	60	25	25	13	5	105	UTX  BM-150M12
185	18	60	30	36	13	7	130	UTX  BM-185M12
185	18	60	30	30	13	6	130	UTX  BM-185M12
240	22	65	32	36	13	7	135	UTX  BM-240M12
240	22	65	32	30	13	6	135	UTX  BM-240M12
300	23.5	70	35	36	13	7	140	UTX  BM-300M12
300	23.5	70	35	35	17	7	140	UTX  BM-300M16
400	26.5	75	35	36	13	7	145	UTX  BM-400M12
400	26.5	75	35	36	17	7	145	UTX  BM-400M16
500	30	70	47	60	-	10	175	UTX  BM-500B
630	34	70	54	60	-	10	175	UTX  BM-630B
800	39	115	54	160	-	10	220	UTX  BM-800B

Conductive Material :

Aluminium Barrel       99.6%
Copper Palm             99.95%
Final Metal State        Fully Annealed including joint.
Joining Method          Friction Welding
Finish                         Natural

Conductivity :

Aluminium      61.8% IACS (MIN)
Copper          99.7% IACS

Aluminium barrel are chemically treated to reduce contact resistance and corrosion and are filled electrically conductive corrosion inhabitant with a jointing compound and capped.

Note :

1. Combinations of Bi-metallic compression joints are designed on the basis of current carrying capacity of individual cables.

2. In case additional combinations are required same may be provided against specific request.

3. Shape, size and dimension are subject to change without notice.