Bimetallic Compression Reducers

MM2 Aluminium	MM2 Copper	D	A1	A2	L	Cat. No.
50	16	20	9	5.5	107	UTX BMC-50/16
50	25	20	9	6.5	107	UTX BMC-50/25
50	35	20	9	8	107	UTX  BMC-50/35
50	50	20	9	9.5	107	UTX BMC-50/50
70	35	20	11	8	107	UTX BMC-70/35
70	50	20	11	9.5	107	UTX BMC-70/50
70	70	20	11	11	107	UTX BMC-70/75
95	35	20	12.5	8	107	UTX BMC-95/35
95	50	20	12.5	9.5	107	UTX BMC-95/50
95	70	20	12.5	11	107	UTX BMC-95/70
95	95	20	12.5	13	107	UTX BMC-95/95
120	50	25	13.7	9.5	133.5	UTX BMC-120/50
120	70	25	13.7	11	133.5	UTX BMC-120/70
120	95	25	13.7	13	133.5	UTX BMC-120/95
120	120	25	13.7	14.2	133.5	UTX BMC-120/120
150	70	25	15.5	11	133.5	UTX BMC-150/70
150	95	25	15.5	13	133.5	UTX BMC-150/95
150	120	25	15.5	14.2	133.5	UTX BMC-150/120
150	150	25	15.5	16	133.5	UTX BMC-150/150
150	185	25	15.5	18	133.5	UTX BMC-150/185
150	95	32	17	13	144	UTX BMC-185/95
185	120	32	17	14.2	144	UTX BMC-185/120
185	150	32	17	16	144	UTX BMC-185/150
185	185	32	17	18	144	UTX BMC-185/185
240	95	32	19.5	13	144	UTX BMC-240/95
240	120	32	19.5	14.2	144	UTX BMC-240/120
240	150	32	19.5	16	144	UTX BMC-240/150
240	185	32	19.5	18	144	UTX BMC-240/185
240	240	32	19.5	20	144	UTX BMC-240/240

Conductive Material :

Aluminium Barrel       99.6%
Copper Palm             99.95%
Final Metal State        Fully Annealed including joint.
Joining Method          Friction Welding
Finish                         Natural

Conductivity :

Aluminium      61.8% IACS (MIN)
Copper          99.7% IACS

Aluminium barrel are chemically treated to reduce contact resistance and corrosion and are filled electrically conductive corrosion inhabitant with a jointing compound and capped.

Note :

1. Combinations of Bi-metallic compression joints are designed on the basis of current carrying capacity of individual cables.

2. In case additional combinations are required same may be provided against specific request.

3. Shape, size and dimension are subject to change without notice.